Upgrading of pyrolytic oil from pyrolytic catalysis cracking (PCC) of waste cooking oil by in situ hydrodeoxygenation (deoxygenation) over nickel-doped HZSM-5. |
| วัน/เดือน/ปี ที่เผยแพร่ |
16 มีนาคม 2566 |
| การประชุม |
| ชื่อการประชุม |
he 32nd Thai Institute of Chemical Engineering and Applied Chemistry Conference TIChE2023, |
| หน่วยงาน/องค์กรที่จัดประชุม |
the Department of Chemical Engineering, Silpakorn University. |
| สถานที่จัดประชุม |
Mida Grande Hotel Dhavaravati |
| จังหวัด/รัฐ |
Nakhon Pathom |
| ช่วงวันที่จัดประชุม |
16 มีนาคม 2566 |
| ถึง |
17 มีนาคม 2566 |
| Proceeding Paper |
| Volume (ปีที่) |
2023 |
| Issue (เล่มที่) |
CATA-P-05 |
| หน้าที่พิมพ์ |
58 |
| Editors/edition/publisher |
- |
| บทคัดย่อ |
The purpose of the work is to upgrade pyrolytic oil from pyrolytic catalysis cracking (PCC) to reduce acidity and oxygen contents by using in-situ hydrodeoxygenation (deoxygenation) using methanol as an in situ hydrogen donor. The reaction condition of work was tested at varying temperatures of 210, 220,230 °C and time of 3,6,9,12 h. The study effect of differences from Nickel (II) nitrate (Ni (NO3)2·6H2O (97.0% purity) reduce oxidation state to get nickel (Ni0) by horizontal tube furnace at a temperature of 550 °C for 5 h under an atmospheric of 10% H2 mixed with 90% N2. loading (0, 3, 6, 9, and 12wt%) on support HZSM-5 (SiO2/Al2O3 = 40) were examined by using the incipient wetness impregnation method. The physical and chemical properties of catalysts were characterized by XRF, XRD, N2 adsorption-desorption, TGA, FESEM, EDS, FTIR, XPS, and XANES. The upgrading oil products were analyzed using density (ASTM D1480-07), viscosity (ASTM D445 D240), HHV (ASTM D2015), total acid number (TAN) (ASTM D664), CHNO, GC-MS, TGA, and FTIR. The best upgrading oil was distilled following ASTM D86 to separate bio-gasoline, bio-kerosene, and bio-diesel. The acidity, density, HHV, and viscosity were done to compare bio-fuel before and after upgrading. The results were shown that NiO/HZSM5 could be successfully reduced to Ni/HZSM5 confirmed by XRD, FTIR, XPS, and XANES. The morphology of catalysts displayed in a spherical shape and agglomerated in higher Ni loading of more than 12%. The Ni contents were effect by the hydrodeoxygenation (HDO) reaction. The optimal Ni loading was about 12% giving the lowest oxygen content in upgrading oil products. However, the reduced oxygen contents of more than 82% compared with raw material pyrolytic oil from pyrolytic catalysis cracking (PCC) condition 3 wt% K2O-MgO/CaO 525 °C.
Keywords: Keywords: In-situ hydrodeoxygenation, Acidity, Sub-critical condition, Pyrolytic catalysis cracking (PCC), Deoxygenation. |
| ผู้เขียน |
|
| การประเมินบทความ (Peer Review) |
ไม่มีผู้ประเมินอิสระ |
| มีการเผยแพร่ในระดับ |
นานาชาติ |
| รูปแบบ Proceeding |
Abstract |
| รูปแบบการนำเสนอ |
Poster |
| เป็นส่วนหนึ่งของวิทยานิพนธ์ |
เป็น |
| ใช้สำหรับสำเร็จการศึกษา |
ไม่เป็น |
| ผลงานที่นำเสนอได้รับรางวัล |
ไม่ได้รับรางวัล |
| แนบไฟล์ |
|
| Citation |
0
|
|
|
|
|
|
|
|
|
การเผยแพร่ในรูปของบทความวารสารทางวิชาการ
English