Cutting performances and wear characteristics of WC inserts coated with TiAlSiN and CrTiAlSiN by filtered cathodic arc in dry face milling of cast iron |
| วัน/เดือน/ปี ที่ได้ตอบรับ |
14 พฤษภาคม 2561 |
| วารสาร |
| ชื่อวารสาร |
The International Journal of Advanced Manufacturing |
| มาตรฐานของวารสาร |
ISI |
| หน่วยงานเจ้าของวารสาร |
springer |
| ISBN/ISSN |
|
| ปีที่ |
|
| ฉบับที่ |
|
| เดือน |
|
| ปี พ.ศ. ที่พิมพ์ |
2561 |
| หน้า |
|
| บทคัดย่อ |
The aim of this work was to study the cutting performances and wear characteristics of Co-WC inserts coated with TiAlSiN and
CrTiAlSiN by a filtered cathodic arc process in dry face milling of cast iron. Face milling experiments were conducted on turbine
cast iron workpieces with TiAlSiN-coated, CrTiAlSiN-coated and uncoated inserts at various cutting speeds and numbers of inserts.
The results showed that Ti-based coatings offered substantially better cutting performances for Co-WC inserts and could effectively
protect the inserts over longer cutting lengths than uncoated ones. Specifically, the CrTiAlSiN coating offered the best cutting
performances with the lowest workpiece surface roughness, the lowest flank wear rate and the longest maximum cutting length of
10 m, which was about 2.5 times as high as that of uncoated one owing to superior hardness relative to yielding and chemical
properties. In addition, the workpiece quality in term of surface roughness was found to improve with increasing cutting speed in the
range of 140–300 m/min and decreasing number of inserts ranging from 1 to 3. Microstructural analyses suggested that the
CrTiAlSiN-coated inserts exhibited wear due to thermal cracking and partial delamination under high temperature ploughing
abrasion while the TiAlSiN-coated ones displayedmainly ploughing abrasive flankwear behaviour,which resulted in a substantially
lower flank wear rate than uncoated WC inserts that suffered from the combination of direct cutting and ploughing abrasive wear. |
| คำสำคัญ |
Titanium-based coating . Filtered cathodic arc . Dry face milling tools .Wear resistanc |
| ผู้เขียน |
|
| การประเมินบทความ |
มีผู้ประเมินอิสระ |
| สถานภาพการเผยแพร่ |
ตีพิมพ์แล้ว |
| วารสารมีการเผยแพร่ในระดับ |
นานาชาติ |
| citation |
ไม่มี |
| เป็นส่วนหนึ่งของวิทยานิพนธ์ |
เป็น |
| แนบไฟล์ |
|
| Citation |
0
|
|
|
ข้อมูลการเผยแพร่ผลงาน
การเผยแพร่ในรูปของบทความวารสารทางวิชาการ
English