Effect of Resin Infiltration Combined with Resin Sealant on Surface Hardness of Enamel Exposed to Chlorinated Water: in vitro Study |
| วัน/เดือน/ปี ที่เผยแพร่ |
18 พฤศจิกายน 2560 |
| การประชุม |
| ชื่อการประชุม |
the 65th Annual Meeting of JADR |
| หน่วยงาน/องค์กรที่จัดประชุม |
Japanese Association for Dental Research |
| สถานที่จัดประชุม |
Showa University |
| จังหวัด/รัฐ |
Tokyo |
| ช่วงวันที่จัดประชุม |
18 พฤศจิกายน 2560 |
| ถึง |
19 พฤศจิกายน 2560 |
| Proceeding Paper |
| Volume (ปีที่) |
2017 |
| Issue (เล่มที่) |
1 |
| หน้าที่พิมพ์ |
111 |
| Editors/edition/publisher |
Ryutaro Kamijo |
| บทคัดย่อ |
Proposal Title: Effect of Resin Infiltration Combined with Resin Sealant on Surface Hardness of Enamel Exposed to Chlorinated Water: in vitro Study
Rationales: Enamel erosion remains a major oral health problem in Thai competitive swimmers, due to chronic exposing to acidic chlorinated water in swimming pools. Progressive tooth surface loss induces sensitivity and causes esthetic concern. Surface protection for these teeth is necessary to prevent further tooth wear and alleviate symptoms.
Objectives: To evaluate effects of low-viscosity resin on infiltration into erosive lesion, combined with resin sealant coating on enamel surface, against enamel erosion-abrasion induced by prolonged exposure to chlorinated water and by tooth brushing.
Methods: Thirty intact human premolars were assigned to three groups and treated as follows: Without treatment (Control), Resin infiltration (ICON) and Resin infiltration Combined with Resin Sealant (ICON-Sealant). Enamel surface erosion was created using acidic chlorinated water for two hours prior to apply the materials. Specimens were subjected to erosive and abrasive cycling for 30 days: brushed by electric-toothbrush for 30 seconds twice a day, immersed in chlorinated water for 2 hours and immersed in artificial saliva for 22 hours. Enamel surface microhardness was measured using a Vickers hardness tester at baseline, after erosion by chlorinated water and after finish erosive and abrasive cycling. The mean different surface microhardness between after erosion and after finish the cycling was analyzed using a one-way ANOVA.
Results: After 30 days of erosive and abrasive cycles, the mean different surface microhardness of ICON-Sealant group (4.04±13.03) was statistical significantly less than ICON group (26.79±15.76; p=0.006) and control group (39.30±28.48; p < 0.001)
Conclusion: Although surface microhardness in all groups had reduced after 30-days erosive and abrasive cycling, the use of ICON combined with Sealant provided more surface protection against erosion and abrasion than using ICON alone or no treatment. Resin Infiltration combined with sealant may be a treatment option for enamel erosion by providing protective coating on eroded surfaces and prevent further loss.
|
| ผู้เขียน |
|
| การประเมินบทความ (Peer Review) |
ไม่มีผู้ประเมินอิสระ |
| มีการเผยแพร่ในระดับ |
นานาชาติ |
| รูปแบบ Proceeding |
Abstract |
| รูปแบบการนำเสนอ |
Poster |
| เป็นส่วนหนึ่งของวิทยานิพนธ์ |
เป็น |
| ผลงานที่นำเสนอได้รับรางวัล |
ไม่ได้รับรางวัล |
| แนบไฟล์ |
|
| Citation |
14
|
|
|
ข้อมูลการเผยแพร่ผลงาน
การเผยแพร่ในรูปของบทความวารสารทางวิชาการ
English