| Title of Article |
Hardness and tribological properties of electrodeposited Ni-P multilayer coatings fabricated through a stirring time-controlled technique |
| Date of Acceptance |
23 May 2022 |
| Journal |
| Title of Journal |
Journal of Materials Research and Technology |
| Standard |
ISI |
| Institute of Journal |
Brazil |
| ISBN/ISSN |
2238-7854 |
| Volume |
2022 |
| Issue |
19 |
| Month |
July-August |
| Year of Publication |
2022 |
| Page |
1884-1896 |
| Abstract |
Ni-P multilayer coatings were deposited on the surfaces of low-carbon steel by direct current electrodeposition through a stirring-time controlled technique (STT). The microstructure, hardness, friction coefficient and wear properties of the deposits were investigated. Scanning electron microscopy (SEM) in back-scattered electron mode revealed multilayer structures of Ni-P coatings fabricated by repeatedly turning the magnetic stirrer
in the bath on and off. Energy dispersive X-ray spectroscopy (EDS) was employed to quantitatively compare the P content in the alternating layers. The hardness of the Ni-P multilayer coatings was found to be significantly greater than that of monolithic Ni-P
coatings. A maximum hardness value of 580 ± 8.7 HV0.1 was found in the sample prepared using the on- and off-stirring periods of 8 and 15 min, respectively. This showed an increased hardness of 20.1% from that of sample prepared with the stirrer turned off. The
Ni-P multilayer coatings prepared by STT also had superior wear resistance to that of monolithic Ni-P coatings. |
| Keyword |
Ni-P coating Electrodeposition Multilayer Tribological properties |
| Author |
|
| Reviewing Status |
มีผู้ประเมินอิสระ |
| Status |
ตีพิมพ์แล้ว |
| Level of Publication |
นานาชาติ |
| citation |
true |
| Part of thesis |
true |
| Attach file |
|
| Citation |
0
|
|
|
Publication
Journal Publication
ไทย