Effect of heat treatment on microstructural characteristics and mechanical properties of hypereutectic B390 aluminium alloys modified by phosphorus and bismuth |
| วัน/เดือน/ปี ที่ได้ตอบรับ |
20 กุมภาพันธ์ 2567 |
| วารสาร |
| ชื่อวารสาร |
Materials Research Express |
| มาตรฐานของวารสาร |
ISI |
| หน่วยงานเจ้าของวารสาร |
IOPscience |
| ISBN/ISSN |
ISSN: 2053-1591 |
| ปีที่ |
Volume 11 |
| ฉบับที่ |
Number 2 |
| เดือน |
February |
| ปี พ.ศ. ที่พิมพ์ |
2567 |
| หน้า |
|
| บทคัดย่อ |
Abstract
This study investigated the effects of solution treatment and aging processes on microstructural
characteristics and mechanical properties of hypereutectic B390 Al-Si Alloy modified by phosphorus
(P) and bismuth (Bi). The morphology evolution of primary Si, eutectic Si, intermetallic compounds,
and secondary dendrite arm spacing (SDAS) of both initial and modified alloys were investigated in ascast
and heat-treated conditions. It was found that the combination of 0.1 wt%P and 0.5 wt%Bi in
B390 alloy resulted in a remarkable modification and refinement of primary Si, eutectic Si, and SDAS
compared to initial specimens in the as-cast condition. After heat treating, the fine lamellar eutectic Si
and intermetallic compounds underwent a higher degree of fragmentation and coarsening, appearing
as small round particles, leading to a more pronounced formation of a supersaturated solid solution.
Additionally, the peak aging time of the B390-P-Bi alloy was only 7 h, 2 h less than the initial specimen.
After T6 treatment and addition of both 0.1 wt%P and 0.5 wt%Bi, the B390-P-Bi alloy exhibited a
smaller rounded Mg3Bi2 phase at peak aging with a 62.07% size reduction compared to the B390-Bi
alloy. The results show that adding P with Bi enhanced hardness, ultimate tensile strength (UTS) and
elongation because of refinement of the SDAS, primary Si and eutectic Si. These refinements played a
crucial role in increasing tensile strength by more effective strengthening through precipitation and
grain size reduction. The B390-P-Bi alloy is a promising choice for applications requiring a balance
between strength and ductility. |
| คำสำคัญ |
hypereutectic Al-Si alloy, modification, tensile properties, phosphorus, bismuth |
| ผู้เขียน |
|
| การประเมินบทความ |
มีผู้ประเมินอิสระ |
| สถานภาพการเผยแพร่ |
ตีพิมพ์แล้ว |
| วารสารมีการเผยแพร่ในระดับ |
นานาชาติ |
| citation |
ไม่มี |
| เป็นส่วนหนึ่งของวิทยานิพนธ์ |
เป็น |
| แนบไฟล์ |
|
| Citation |
0
|
|
|
|
|
|
|
|
|
การเผยแพร่ในรูปของบทความวารสารทางวิชาการ
English